textile auxiliary agentsvarious industrial useEBOLIT 105
bonding agent for the production of epoxy coating masses with high utility properties (ground anticorrosive dye, burning-out varnishes, impregnation of concrete, coatings of metallic and wooden surfaces etc.Product characteristics
It is a solution of low-molecular epoxy resin in a blend of an organic disslovent.
Use
It is used as bonding agent for the production of epoxy coating masses with high utility properties such as ground anticorrosive dye, burning-out varnishes, impregnation of concrete, coatings of metallic and wooden surfaces. As a hardening agent Hardener T 150, Hardener T 156, Hardener T 2605 can be used.
Product features
It is a light-yellow viscous liquid with a specific odour.
| Properties of the composition of EBOLIT 105 : HARDENER T 150 Miscible ratio 100 : 60 | |
| Composition lifetime | 10 hours maximally |
| Properties of hardened coating | |
| Stage of drying S 1 | 1,5 hour maximally |
| Stage of drying S 5 | 8 hours maximally |
| Coating hardened during lab temperature Pendulum-tested hardness after 10 days | 50 % minimally |
Content of organic solvents
| characteristic | Unit | value |
| Density of product | g.cm-3 | 1,055 |
| Content of organic dissolvent expressed in weight decimal | kg/kg of product | 0,304 |
| Content of the overall organic carbon | kg/kg of product | 0,304 |
| Content of non-volatile substanec expressed in volumic % | volumic % | 68,7 |
EBOLIT 105 must comply with these quality signs:
| Quality sign | Value | Methodology of setting |
| Content of non-volatile substances (%) | 74 to 76 | PN-ZM 567/2010 |
| Epoxy equivalent in dry matter (g.mol-1) | 1,8 to 2,1 | ČSN EN ISO 3001 |
| Epoxy index (mol/1000g) | 476 to 555 | ČSN EN ISO 3001 |
| Viscosity at 25 oC (mPa.s) | 3 to 6 | PN-ZM 567/2010 |
Product manufacturing
For the application purposes, EBOLIT 105 is hardened by following hardeners to 100 weight points of EBOLIT 105:
| HARDENER T 150 | 60 weight points |
| HARDENER T 156 | 60 weight points |
| HARDENER T 2605 | 18,5 weight points |
Packing and storage
EBOLIT 105 is filled up to a metallic drums (200 litres) or to other containers that have been discussed in advance. This product is stored in closed containers at the places protected from direct climatic influences. The recommended storage temperature is between +5 to + 30 oC. It must not be exposed to direct sunshine nor close to any sources of heat. Storage temperatures below 0 oC do not have any negative effect on the application characteristics of the product.
Transport
EBOLIT 105 is transported in compliance with the ADR/RID regulations.
Warranty
If the product is transported and stored according to the above mentioned conditions, the warranty is 6 months from the date of stock-out.
Note
Data about the product characteristics and its manufacturing were acquired by laboratory measurements and application tests. This technical sheet can only give a legal
advice without any obligation. The manufacturing of the product must be adjusted to the specific conditions.
| Properties | two-component organic coating, interior application, dilutable coatings |
|---|