Solution of medium molecular weight epoxy resin in mixture of organic diluents

Product characteristics

Solution of medium molecular weight epoxy resin in mixture of organic diluents.


EBOLIT 102 (component A) is used for preparation of epoxy varnishes and epoxy coating compositions suitable for interior application. It is intended for application to wood, wood based products and matters, concrete, masonry, gypsum boards and metals. HARDENER T 156 (component B) is used as a hardening component.

Product Features

Light yellow coloured moderately viscous liquid with a characteristic smell that can be diluted with acetone, xylene or isobutanol.

Organic solvent content




product's density


Content of organic solvents (expressed in mass fraction)

kg/kg of the product


Total organic carbon content

kg/kg of the product


Content of nonvolatile substances (expressed in volume percent)

volume percent


 EBOLIT 102 must comply with the following quality characteristics:

Quality characteristic 


Methodology of assessment

Content of nonvolatile substances (%)

60 ± 2.5

PN-ZM 137/2001

Epoxy equivalent in dry matter (g.mol-1)           

445 to 525


Epoxy index (mol/1000 g)

1.90 to 2.24


Consistency at 23 °C (in s; measured by an efflux cup 4 mm)

80 to 150


Colour in mg J2/100 cm3

maximally 3

ČSN 67 3011


Properties of EBOLIT 102 (component A) composition: HARDENER T 156 (component B)

 Mixing ratio 100 : 50 

Working life of the composition

maximally 12 hours


Hardened coating features 

Relative humidity

60 to 70 %

Drying stage of S 1      

maximally 3 hours

Drying stage S 5                                              

maximally 24 hours

Coating hardened at laboratory temperature

Hardness (measured by a pendulum 3 days after it hardened)


minimally 40 %

 Surface preparation

Prior to EBOLIT 102 application, it is necessary to prepare a treated surface. It must be void of mechanical impurities or grease. If necessary, it must be ground. It is also possible to use a penetration membrane as a preliminary treatment, especially in case of a concrete bedding. We recommend using a penetration composition EBOLIT 101.

Directions for Use

EBOLIT 102 is used as a coating composition in the above mentioned applications. To prepare a varnish, the component A and the component B are mixed in a ratio of 100 units (component A) to 50 units (component B). Before they are used, the ­components must be thoroughly stirred. Consistency of the obtained mixture can be adjusted in accordance to a chosen method of application by use of a xylene-butanol mixture, isobutanol (4:1) or the diluent S 6003.EBOLIT 102


Usage of an EBOLIT 102 composition for 1 m2 is 80 g.m-2 for a single coating. We recommend to perform from 2 to 3 coatings depending on absorptivity of the treated materiál.

Packaging & Storage

EBOLIT 102 is delivered in 200 l metallic barrels. Alternatively, it can be delivered in different containers that were discussed and agreed on in advance. Store it in a sealed container in places protected from direct climatic influences. Recommended storage temperature is between +5 to +30 °C. Must not be stored in the sun or near heat sources. Storing at temperatures below 0 °C does not affect product's application properties.


EBOLIT 102 is transported by covered vehicles in compliance with ADR/RID Regulations.


Provided the product is transported and stored in accordance with the above written conditions, its warranty is 6 months from the date it was delivered from a warehouse.


Data about the product characteristics and its processing were obtained by laboratory measurements and application tests. This technical data sheet can provide solely legal advice without any engagements. Use of the product should be always adjusted to specific conditions.


Propertiestwo-component organic coating, interior application, dilutable coatings